RESIDUAL STRESS AND HIGH-TEMPERATURE MECHANICAL BEHAVIOR OF THERMAL BARRIER COATED TURBINE BLADES

Hao Yiyi; Liang Lihong; Qiu Tian

doi:10.6052/0459-1879-23-021

Volume 55 Issue 6

Jun. 2023

Turn off MathJax

Article Contents

Abstract

References

Chinese Journal of Theoretical and Applied Mechanics > 2023 > 55(6): 1319-1328. > DOI: 10.6052/0459-1879-23-021 CSTR: 32045.14.0459-1879-23-021

Hao Yiyi, Liang Lihong, Qiu Tian. Residual stress and high-temperature mechanical behavior of thermal barrier coated turbine blades. Chinese Journal of Theoretical and Applied Mechanics, 2023, 55(6): 1319-1328. DOI: 10.6052/0459-1879-23-021

Citation:

PDF (2758 KB)

RESIDUAL STRESS AND HIGH-TEMPERATURE MECHANICAL BEHAVIOR OF THERMAL BARRIER COATED TURBINE BLADES

College of Mechanical and Electrical Engineering, Beijing University of Chemical Technology, Beijing 100029, China

Received Date: January 15, 2023
Accepted Date: April 19, 2023
Available Online: April 20, 2023

Graphical Abstract

Abstract

Abstract

Thermal barrier coated turbine blades can effectively improve the thermal efficiency and performance of aero-engines. They exert significant importance on security and stability of aero-engines. In the process of thermal shock service, the thermal barrier coating system is prone to various forms of damage such as surface cracks and interface cracks, which seriously affects the service stability of turbine blades. Considering that the residual stress generated during the preparation of turbine blades with thermal barrier coating will have a great impact on the quality of thermal barrier coating, this work firstly studied the residual deformation and stress during the natural convection cooling process after the thermal barrier coating was deposited into turbine blades with certain shape by using the finite element method. Furthermore, the temperature and stress state of turbine blades with thermal barrier coating under high temperature thermal shock were simulated and analyzed, and the stress mechanism of mechanical behavior difference between blade with thermal barrier coating and alloy blade without thermal barrier coating under high temperature was revealed. The results show that the distribution of deformation and residual stress after the preparation of thermal barrier coating blade is complex due to the geometrical structure of the curvature blade, and the maximum local compressive stress at the blade root is close to 200 MPa. The thermal barrier coating can provide obvious thermal protection for the blade under high temperature service, and the maximum Mises stress can be reduced 600 MPa, but the thermal protection effect in the trailing edge area is limited. The maximum principal stress in the suction surface near the trailing edge of the ceramic coated blade root reaches 159.5 MPa. Therefore, the thermal barrier coating turbine blade in high temperature service will preferentially show higher stress in the blade root and trailing edge of the ceramic layer, which becomes the starting position of crack initiation, propagation and spalling.
- turbine blade,
- thermal barrier coating,
- temperature load,
- residual stress,
- deformation in high temperature

FullText(HTML)

References (39)

References

[1]	向丰, 何旺, 董洋等. 航空发动机参数自动判读和监控系统设计. 机电工程技术, 2022, 51(8): 149-152, 211 (Xiang Feng, He Wang, Dong Yang, et al. Design of automatic interpretation and monitoring system for aeroengine parameters. Mechanical and Electrical Engineering Technology, 2022, 51(8): 149-152, 211 (in Chinese) Xiang Feng, He Wang, Dong Yang et al. Design of automatic interpretation and monitoring system for aeroengine parameters. Mechanical and electrical engineering technology, 2022, 51(08): 149-152 + 211(in Chinese))
[2]	刘国库, 王威. 航空发动机叶片制造及再制造技术研究. 科技创新与应用, 2022, 12(33): 145-148 (Liu Caiguo, Wang Wei. Research on manufacturing and remanufacturing technology of aero engine blade. Scientific and Technological Innovation and Application, 2022, 12(33): 145-148 (in Chinese) Liu Caiguo, Wang Wei. Research on manufacturing and remanufacturing technology of aero engine blade. Scientific and technological innovation and application, 2022, 12(33): 145-148(in Chinese))
[3]	冯乐然. 民用航空发动机涡轮叶片材料研究. 中国设备工程, 2022, 38(7): 268-269 (Feng Leran. Research on turbine blade materials of civil aero engine. China Equipment Engineering, 2022, 38(7): 268-269 (in Chinese) doi: 10.3969/j.issn.1671-0711.2022.07.146 Feng Leran. Research on turbine blade materials of civil aero engine. China Equipment Engineering, 2022, 38(07): 268-269(in Chinese)) doi: 10.3969/j.issn.1671-0711.2022.07.146
[4]	Bose S, Demasi-Marcin J. Thermal barrier coating experience in gas turbine engines at Pratt & Whitney. Journal of Thermal Spray Technology, 1997, 6(1): 99-104 doi: 10.1007/BF02646318
[5]	李定骏, 杨镠育, 孙帆等. 预热温度对热障涂层表面裂纹形成的影响. 航空学报, 2022, 43(6): 338-347 (Li Dingjun, Yang Liayu, Sun Fan, et al. Effect of preheating temperature on surface crack formation of thermal barrier coatings. Journal of Aeronautics, 2022, 43(6): 338-347 (in Chinese) Li Dingjun, Yang Liayu, Sun Fan et al. Effect of preheating temperature on surface crack formation of thermal barrier coatings. Journal of Aeronautics, 2022, 43(06): 338-347(in Chinese))
[6]	蔡书汉. EB-PVD制备热障涂层工艺对其微观结构与性能影响的研究. [硕士论文]. 湘潭: 湘潭大学, 2021 Cai Shuhan. Effect of EB-PVD preparation process on microstructure and properties of thermal barrier coatings. [Master Thesis]. Xiangtan: Xiangtan University, 2021 (in Chinese))
[7]	付娜. 某航空发动机涡轮盘和叶片的强度分析与寿命计算. [硕士论文]. 西安: 西北工业大学, 2006 Fu Na. Strength analysis and life calculation of turbine discs and blades of an aero engine. [Master Thesis]. Xi’an: Northwestern Polytechnical University, 2006 (in Chinese))
[8]	周益春, 杨丽, 刘志远等. 涡轮叶片热障涂层隔热效果的研究进展. 中国材料进展, 2020, 39(10): 707-722, 738 (Zhou Yichun, Yang Li, Liu Zhiyuan, et al. Research progress on thermal insulation effect of thermal barrier coatings on turbine blades. Progress in Materials in China, 2020, 39(10): 707-722, 738 (in Chinese) doi: 10.7502/j.issn.1674-3962.202007035 Zhou Yichun, Yang Li, Liu Zhiyuan et al. Research progress on thermal insulation effect of thermal barrier coatings on turbine blades. Progress in Materials in China, 2020, 39(10): 707-722 + 738(in Chinese)) doi: 10.7502/j.issn.1674-3962.202007035
[9]	杨晓军, 于天浩, 胡英琦等. 沉积环境下涡轮叶片前缘气膜冷却的实验研究. 北京航空航天大学学报, 2021, 47(11): 2189-2199 (Yang Xiaojun, Yu Tianhao, Hu Yingqi, et al. Experimental study on leading edge gas film cooling of turbine blades in depositional environment. Journal of Beijing University of Aeronautics and Astronautics, 2021, 47(11): 2189-2199 (in Chinese) Yang Xiaojun, Yu Tianhao, Hu Yingqi et al. Experimental study on leading edge gas film cooling of turbine blades in depositional environment. Journal of Beijing University of Aeronautics and Astronautics, 2021, 47(11): 2189-2199(in Chinese))
[10]	陈博, 朱剑寒, 鲁辉军. 航空发动机涡轮叶片高周疲劳裂纹故障分析与思考. 燃气涡轮试验与研究, 2020, 33(3): 33-36 (Chen Bo, Zhu Jianhan, Lu Huijun. Failure analysis and consideration on high cycle fatigue crack of aero engine turbine blade. Gas Turbine Test and Research, 2020, 33(3): 33-36 (in Chinese) doi: 10.3969/j.issn.1672-2620.2020.03.007 Chen Bo, Zhu Jianhan, Lu Huijun. Failure analysis and consideration on high cycle fatigue crack of aero engine turbine blade. Gas Turbine Test and Research, 2020, 33(03): 33-36(in Chinese)) doi: 10.3969/j.issn.1672-2620.2020.03.007
[11]	Andrei L, Andreini A, Facchini B, et al. A decoupled CHT procedure: Application and validation on a gas turbine vane with different cooling configurations. Energy Procedia, 2014, 45(1): 1087-1096
[12]	吴志渊, 闫寒, 吴林潮等. 旋转裂纹叶片-弹性轮盘耦合系统振动特性分析. 航空学报, 2022, 43(9): 109-122 (Wu Zhiyuan, Yan Han, Wu Linchao, et al. Analysis of vibration characteristics of rotating crack blade-elastic roulette coupling system. Journal of Aeronautics and Astronautics, 2022, 43(9): 109-122 (in Chinese) Wu Zhiyuan, Yan Han, Wu Linchao et al. Analysis of vibration characteristics of rotating crack blade-elastic roulette coupling system. Journal of Aeronautics and Astronautics, 2022, 43(09): 109-122(in Chinese))
[13]	Krishnamurthy R, Srolovitz DJ. Sintering and microstructure evolution in columnar thermal barrier coatings. Acta Materialia, 2009, 57(4): 1035-1048 doi: 10.1016/j.actamat.2008.10.053
[14]	Tsipas SA. Effect of dopants on the phase stability of zirconia-based plasma sprayed thermal barrier coatings. Journal of the European Ceramic Society, 2010, 30(1): 61-72 doi: 10.1016/j.jeurceramsoc.2009.08.008
[15]	Wang L, Li DC, Yang JS, et al. Modeling of thermal properties and failure of thermal barrier coatings with the use of finite element methods: A review. Journal of the European Ceramic Society, 2016, 36(6): 1313-1331 doi: 10.1016/j.jeurceramsoc.2015.12.038
[16]	Liu QM, Huang SZ, He AJ. Composite ceramics thermal barrier coatings of yttria stabilized zirconia for aero-engines. Journal of Materials Science & Technology, 2019, 35(12): 2814-2823
[17]	Sohn YH, Lee EY, Nagaraj BA, et al. Microstructural characterization of thermal barrier coatings on high pressure turbine blades. Surface & Coatings Technology, 2001, 146(146-147): 132-139
[18]	伍杰, 朱旺, 毛祖莉. 热循环下热障涂层热生长氧化层生长规律研究. 中国陶瓷, 2021, 57(11): 32-39 (Wu Jie, Ju Wang, Mao Zuli. Study on the growth law of oxidation layer of thermal barrier coating under thermal cycling. China Ceramics, 2021, 57(11): 32-39 (in Chinese) doi: 10.16521/j.cnki.issn.1001-9642.2021.11.005 Wu Jie, Ju Wang, Mao Zuli. Study on the growth law of oxidation layer of thermal barrier coating under thermal cycling. China Ceramics, 2021, 57(11): 32-39(in Chinese)) doi: 10.16521/j.cnki.issn.1001-9642.2021.11.005
[19]	由于, 徐健, 燕群等. 涡轮叶片耦合疲劳寿命预测与试验验证. 航空动力学报, 2022, 37(5): 946-953 (You Yu, Xu Jian, Yan Qun, et al. Turbine blade coupling fatigue life prediction and experimental verification. Aeronautical Dynamics Journal, 2022, 37(5): 946-953 (in Chinese) You Yu, Xu Jian, Yan Qun et al. Turbine blade coupling fatigue life prediction and experimental verification. Aeronautical Dynamics Journal, 2022, 37(05): 946-953(in Chinese))
[20]	周益春, 刘奇星, 杨丽等. 热障涂层的破坏机理与寿命预测. 固体力学学报, 2010, 31(5): 504-531 (Zhou Yichun, Liu Qixing, Yang Li, et al. Failure mechanism and life prediction of thermal barrier coating. Chinese Journal of Solid Mechanics, 2010, 31(5): 504-531 (in Chinese) Zhou Yichun, Liu Qixing, Yang Li et al. Failure mechanism and life prediction of thermal barrier coating. Chinese Journal of Solid Mechanics, 2010, 31(05): 504-531(in Chinese))
[21]	Kumar V, Balasubramanian K. Progress update on failure mechanisms of advanced thermal barrier coatings: A review. Progress in Organic Coatings, 2016, 90: 54-82 doi: 10.1016/j.porgcoat.2015.09.019
[22]	Li B, Fan X, Li D, et al. Design of thermal barrier coatings thickness for gas turbine blade based on finite element analysis. Mathematical Problems in Engineering, 2017, 2017: 1-13
[23]	庞铭, 张啸寒. 结构参数对等离子喷涂 Mo/8 YSZ 功能梯度热障涂层残余应力的影响. 航空材料学报, 2020, 40(6): 23-32 (Pang Ming, Zhang Xiaohan. Effect of structural parameters on residual Stress of Mo/8 YSZ functionally gradient thermal barrier coating by plasma spraying. Journal of Aeronautical Materials, 2020, 40(6): 23-32 (in Chinese) Pang Ming, Zhang Xiaohan. Effect of structural parameters on residual Stress of Mo/8 YSZ functionally gradient thermal barrier coating by plasma spraying. Journal of Aeronautical Materials, 2020, 40(06): 23-32(in Chinese))
[24]	徐颖强, 孙戬, 李万钟等. 基于圆筒模型的热障涂层安定分析. 力学学报, 2015, 47(5): 779-788 (Xu Yingqiang, Sun Jian, Li Wanzhong, et al. Stabilization analysis of thermal barrier coating based on cylindrical model. Chinese Journal of Theoretical and Applied Mechanics, 2015, 47(5): 779-788 (in Chinese) doi: 10.6052/0459-1879-15-073 Xu Yingqiang, Sun Jian, Li wanzhong et al. Stabilization analysis of thermal barrier coating based on cylindrical model. Chinese Journal of Mechanics, 2015, 47(05): 779-788(in Chinese)) doi: 10.6052/0459-1879-15-073
[25]	唐健江, 于方丽, 张海鸿等. 热障涂层的界面形貌对TGO层生长行为的作用机制. 航空材料学报, 2019, 39(5): 113-119 (Tang Jianjiang, Yu Fangli, Zhang Haihong, et al. Mechanism of interaction morphology of thermal barrier coatings on the growth behavior of TGO layer. Journal of Aeronautical Materials, 2019, 39(5): 113-119 (in Chinese) Tang Jianjiang, Yu Fangli, Zhang Haihong et al. Mechanism of interaction morphology of thermal barrier coatings on the growth behavior of TGO layer. Journal of Aeronautical Materials, 2019, 39(05): 113-119(in Chinese))
[26]	陈宇慧, 杨晓翔, 钟舜聪. 对流换热对ZrO₂-8%Y₂O₃涂层系统力学性能的影响. 航空材料学报, 2014, 34(5): 63-68 (Chen Yuhui, Yang Xiaoxiang, Zhong Shuncong. Effect of convective heat transfer on mechanical properties of ZrO₂-8%Y₂O₃ coating system. Journal of Aeronautical Materials, 2014, 34(5): 63-68 (in Chinese) Chen Yuhui, Yang Xiaoxiang, Zhong Shuncong. Effect of convective heat transfer on mechanical properties of ZrO_2-8% Y_2 O_3 coating system. Journal of Aeronautical Materials, 2014, 34(05): 63-68(in Chinese))
[27]	Zhu W, Cai M, Yang L, et al. The effect of morphology of thermally grown oxide on the stress field in a turbine blade with thermal barrier coatings. Surface and Coatings Technology, 2015, 276: 160-167 doi: 10.1016/j.surfcoat.2015.06.061
[28]	赵爽. 航空发动机涡轮叶片疲劳可靠性分析. [硕士论文]. 哈尔滨: 哈尔滨工程大学, 2019 Zhao Shuang. Fatigue reliability analysis of aeroengine turbine blades. [Master Thesis]. Harbin: Harbin Engineering University, 2019 (in Chinese))
[29]	Rösler J, Bäker M, Aufzug K. A parametric study of the stress state of thermal barrier coatings: Part I: creep relaxation. Acta Materialia, 2004, 52(16): 4809-4817
[30]	Lugscheider E, Nickel R. Finite element simulation of a coating formation on a turbine blade during plasma spraying. Surface and Coatings Technology, 2003, 174-175: 475-481 doi: 10.1016/S0257-8972(03)00331-1
[31]	Evans AG, Fleck NA, Faulhaber S, et al. Scaling laws governing the erosion and impact resistance of thermal barrier coatings. Wear, 2006, 260(7-8): 886-894
[32]	Crowell MW, Wang J, Mcmeeking RM, et al. Dynamics of kink band formation in columnar thermal barrier oxides. Acta Materialia, 2008, 56(16): 4150-4159 doi: 10.1016/j.actamat.2008.04.058
[33]	孔祥谦, 王传溥. 有限单元法在传热学中的应用. 北京: 科学出版社, 1981 Kong Xiangqian, Wang Chuanfu. Application of Finite Element Method in Heat Transfer. Beijing: Science Press, 1981 (in Chinese))
[34]	Traeger F, Vassen R, Rauwald KH, et al. Thermal cycling setup for testing thermal barrier coatings. Advanced Engineering Materials, 2003, 5(6): 429-432
[35]	Spitsberg I, More K. Effect of thermally grown oxide (TGO) microstructure on the durability of TBCs with PtNiAl diffusion bond coats. Materials Science and Engineering A, 2006, 417(1): 322-333
[36]	Yang L, Liu QX, Zhou YC, et al. Finite element simulation on thermal fatigue of a turbine blade with thermal barrier coatings. Journal of Materials Science & Technology, 2014, 30(4): 371-380
[37]	Ziaei-Asl A, Ramezanlou MT. Thermo-mechanical behavior of gas turbine blade equipped with cooling ducts and protective coating with different thicknesses. International Journal of Mechanical Sciences, 2019, 150: 656-664 doi: 10.1016/j.ijmecsci.2018.10.070
[38]	朱建国, 谢惠民, 刘战伟. 热障涂层力学性能的实验测试方法研究进展. 力学学报, 2013, 45(1): 45-60 (Zhu Jianguo, Xie Huimin, Liu Zhanwei. Research progress of experimental testing methods for mechanical properties of thermal barrier coatings. Chinese Journal of Theoretical and Applied Mechanics, 2013, 45(1): 45-60 (in Chinese) Zhu Jianguo, Xie Huimin, Liu Zhanwei. Research progress of experimental testing methods for mechanical properties of thermal barrier coatings. Chinese Journal of Mechanics, 2013, 45(01): 45-60(in Chinese))
[39]	彭中伏, 陈学军. 热对流作用下筒壁涂层的边裂行为. 力学学报, 2018, 50(2): 307-314 (Peng Zhongfu, Chen Xuejun. Edge cracking behavior of cylinder wall coating under thermal convection. Chinese Journal of Theoretical and Applied Mechanics, 2018, 50(2): 307-314 (in Chinese) Peng Zhongfu, Chen Xuejun. Edge cracking behavior of cylinder wall coating under thermal convection. Chinese Journal of Mechanics, 2018, 50(02): 307-314(in Chinese))

[1]	Gao Zihan, Cheng Xiaoqi, Fan Ziye, Jiang Nan. INVESTIGATION ON THE DISTRIBUTION OF UNIFORM MOMENTUM ZONES WITH VARIABLE-INTERVAL SPATIAL AVERAGE DETECTION[J]. Chinese Journal of Theoretical and Applied Mechanics, 2024, 56(8): 2193-2202. DOI: 10.6052/0459-1879-24-098
[2]	Jiang Xin, Bai Zhengfeng, Ning Zhiyuan, Wang Siyu. INTERVAL UNCERTAINTY ANALYSIS METHODS FOR MULTIBODY SYSTEMS BASED ON SIGNAL DECOMPOSITION AND CHEBYSHEV POLYNOMIALS[J]. Chinese Journal of Theoretical and Applied Mechanics, 2022, 54(6): 1694-1705. DOI: 10.6052/0459-1879-22-092
[3]	Wu Shengchuan, Luo Yan, Wang Wenjing, Li Yongheng, Hu Chunming. FATIGUE STRENGTH AND RESIDUAL LIFETIME ASSESSMENT OF RAILWAY AXLES SUBJECTED TO FOREIGN OBJECT DAMAGE[J]. Chinese Journal of Theoretical and Applied Mechanics, 2021, 53(1): 84-95. DOI: 10.6052/0459-1879-20-228
[4]	Wu Pengge, Ni Bingyu, Jiang Chao. AN INTERVAL FINITE ELEMENT METHOD BASED ON THE NEUMANN SERIES EXPANSION[J]. Chinese Journal of Theoretical and Applied Mechanics, 2020, 52(5): 1431-1442. DOI: 10.6052/0459-1879-20-152
[5]	Wang Hao, Ke Shitang. EVOLUTION CHARACTERISTIC AND WORKING MECHANISM ANALYSIS OF ROTATING THIN-WALLED STRUCTURES IN POST-CRITICAL TURBULENT INTERVAL BASED ON FIELD MEASUREMENT[J]. Chinese Journal of Theoretical and Applied Mechanics, 2019, 51(1): 111-123. DOI: 10.6052/0459-1879-18-125
[6]	Liu Jian, Lei Jirong, Xia Baizhan. THE INTERVAL ANALYSIS OF MULTILAYER-METAMATERIALS WITH PERFORATED APERTURES BASED ON CHEBYSHEV EXPANSION[J]. Chinese Journal of Theoretical and Applied Mechanics, 2017, 49(1): 137-148. DOI: 10.6052/0459-1879-16-254
[7]	Ji Xing. A CRITICAL REVIEW ON CRITERIA OF FRACTURE MECHANICS[J]. Chinese Journal of Theoretical and Applied Mechanics, 2016, 48(4): 741-753. DOI: 10.6052/0459-1879-16-069
[8]	Li Qi, Qiu Zhiping, Zhang Xudong. SECOND-ORDER PARAMETER PERTURBATION METHOD FOR DYNAMIC STRUCTURES WITH INTERVAL PARAMETERS[J]. Chinese Journal of Theoretical and Applied Mechanics, 2015, 47(1): 147-153. DOI: 10.6052/0459-1879-14-088
[9]	Qiu Zhiping Qi Wuchao. Collocation interval finite element method[J]. Chinese Journal of Theoretical and Applied Mechanics, 2011, 43(3): 496-504. DOI: 10.6052/0459-1879-2011-3-lxxb2010-382
[10]	Weijie Li, Baolin Wang, Xinhong Zhang. Viscoelastic fracture of a functionally graded material strip[J]. Chinese Journal of Theoretical and Applied Mechanics, 2008, 40(3): 402-406. DOI: 10.6052/0459-1879-2008-3-2006-468

Cited By

Cited by

Periodical cited type(2)

1.	龚海军，郭志启，李福军，钟发勇，高正源，孙鹏飞. 铸钢机车车钩精密铸造工艺及其凝固组织研究. 特种铸造及有色合金. 2024(09): 1291-1296 .
2.	马建勇，马术文，张海柱，黎荣，肖鹏. 面向数字孪生的构架裂纹扩展寿命预测建模分析方法. 机械设计与研究. 2023(05): 172-177 .

Other cited types(6)

Get Citation

PDF

XML

Article Metrics

Article views (889) PDF downloads (121) Cited by(8)

RESIDUAL STRESS AND HIGH-TEMPERATURE MECHANICAL BEHAVIOR OF THERMAL BARRIER COATED TURBINE BLADES

Abstract

References

Related Articles

Cited by

Periodical cited type(2)

Other cited types(6)

Catalog

Article Metrics

Related

Download Center

Author Center

RESIDUAL STRESS AND HIGH-TEMPERATURE MECHANICAL BEHAVIOR OF THERMAL BARRIER COATED TURBINE BLADES

Abstract

References

Related Articles

Cited by

Periodical cited type(2)

Other cited types(6)

Catalog

Article Metrics

Related

Download Center

Author Center

Export File

Citation

Format

Content